ISO 19628:2017 describes two methods for the determination of the specific heat capacity of ceramic matrix composites with continuous reinforcements (1D, 2D, 3D).
Unidirectional (1D), bi-directional (2D) and tridirectional (XD, with 2 < x ≤ 3).
The two methods are:
- method A: drop calorimetry;
- method B: differential scanning calorimetry.
They are applicable from ambient temperature up to a maximum temperature, depending on the method: method A can be used up to 2 250 K, while method B is limited to 1 900 K.
NOTE Method A is limited to the determination of an average value of the specific heat capacity over a given temperature range and can give a larger spread of results.
Общая информация
-
Текущий статус: ОпубликованоДата публикации: 2017-04Этап: Между-народный стандарт подлежит пересмотру [90.92]
-
Версия: 1
-
Технический комитет :ISO/TC 206ICS :81.060.30
- RSS обновления
Жизненный цикл
-
Сейчас
ОпубликованоISO 19628:2017
Стандарт, который пересматривается каждые 5 лет
Этап: 90.92 (Будет пересмотрено)-
00
Предварительная стадия
-
10
Стадия, связанная с внесением предложения
-
20
Подготовительная стадия
-
30
Стадия, связанная с подготовкой проекта комитета
-
40
Стадия, связанная с рассмотрением проекта международного стандарта
-
50
Стадия, на которой осуществляется принятие стандарта
-
60
Стадия, на которой осуществляется публикация
-
90
Стадия пересмотра
-
95
Стадия, на которой осуществляется отмена стандарта
-
00
-
Будет заменено
В стадии разработкиISO/PRF 19628
Появились вопросы?
Ознакомьтесь с FAQ
Часы работы:
Понедельник – пятница: 09:00-12:00, 14:00-17:00 (UTC+1)